https://dspace.uzhnu.edu.ua/jspui/handle/lib/4317| Назва: | Room Temperature Visible Luminescence in Wide Band Gap Chalcogenide Glasses |
| Автори: | Mitsa, V.M. Holomb, R.M. Lovas, G. Ivanda, M. Rudyko, G.Yu. Gule, E.G. Fekeshgazi, I.V. Міца, Володимир Михайлович |
| Ключові слова: | Luminescence, Chalcogenide Glasses |
| Дата публікації: | 2012 |
| Короткий огляд (реферат): | Visible photoluminescence (PL) was observed in binary g-As2S3, technologically modified g-GeS2(TiVj) and ternary glasses along (As2S3)x(GeS2)1-x line. PL maximum in g-As2S3 at 2.43 eV was assigned to band-to-band transitions and its position is in good agreement with value of optical band-gap edge absorption (Eo=2.4 eV). It is suggested that the peak at 2.2-2.3 eV in g-GeS2(TiVj) and GeS2-based ternary glasses may be attributed to presence of GeOx species. Complex PL peak at 2.6-2.7 eV in GeS2-based glasses was identified with germanium sulfur sites. |
| Тип: | Text |
| Тип публікації: | Стаття |
| URI (Уніфікований ідентифікатор ресурсу): | https://dspace.uzhnu.edu.ua/jspui/handle/lib/4317 |
| Розташовується у зібраннях: | Наукові публікації кафедри інформатики та фізико-математичних дисциплін Наукові публікації кафедри інформаційних управляючих систем та технологій |
Файли цього матеріалу:
| Файл | Опис | Розмір | Формат | |
|---|---|---|---|---|
| 22_mipro_proc_2012.pdf | 882.6 kB | Adobe PDF | Переглянути/Відкрити |
Усі матеріали в архіві електронних ресурсів захищені авторським правом, всі права збережені.