https://dspace.uzhnu.edu.ua/jspui/handle/lib/69519| Назва: | Mechanical properties of superionic ceramics based on (Cu1–xAgx)7GeSe5I solid solutions |
| Автори: | Bilanych, V. S. Babilya, M. I. Korovska, D. M. Studenyak, V. I. Shender, I. O. Pogodin, A. I. Studenyak, I. P. Kranjčec, M. |
| Ключові слова: | superionic conductors, solid solution, superionic conductor, cationic substitution, ceramic, microhardness. |
| Дата публікації: | 2021 |
| Видавництво: | Semiconductor Physics, Quantum Electronics & Optoelectronics |
| Бібліографічний опис: | Semiconductor Physics, Quantum Electronics & Optoelectronics. 2021. V. 24, No 4. P. 372-377 |
| Короткий огляд (реферат): | (Cu1–xAgx)7GeSe5I-based ceramics were prepared by pressing and sintering from the micro- and nanopowders. The ceramic samples were investigated using microstructural analysis. The microhardness was measured applying the indentation method with use of the Vickers pyramid. It has been shown that the microhardness of (Cu1–xAgx)7GeSe5I-based ceramics decreases with copper content decrease at Cu+→Ag+cationic substitution. The compositional dependences and size effects of microhardness inherent to (Cu1–xAgx)7GeSe5I-based ceramics have been analyzed. The size effects of microindentation have been interpreted within the framework of the gradient theory of plasticity. |
| Тип: | Text |
| Тип публікації: | Стаття |
| URI (Уніфікований ідентифікатор ресурсу): | https://dspace.uzhnu.edu.ua/jspui/handle/lib/69519 |
| Розташовується у зібраннях: | Наукові публікації кафедри прикладної фізики і квантової електроніки |
Файли цього матеріалу:
| Файл | Опис | Розмір | Формат | |
|---|---|---|---|---|
| 2021 SPQEO (Cu1–xAgx)7GeSe5I-based ceramics.pdf | 632.63 kB | Adobe PDF | Переглянути/Відкрити |
Усі матеріали в архіві електронних ресурсів захищені авторським правом, всі права збережені.